1. Mo-Co-Ni ternary active components, alumina- titania composite carrier.
2. Excellent activity and stability.
3. High mechanical strength and structure stability.
4. Low light off temperature, can be used alone in adiabatic for the high olefin feedstock.
5. Enables start-up without pre-sulfiding, shorten star-up time.
1. Used in hydrogenation purification process of H2 production feedstock for olefin saturation and organic sulfur conversion.
2. AMC-YJ-01/AMC-YJ-03 suitable for purifying natural gas, coking dry gas, catalytic dry gas, hydrogenation dry gas, naphtha etc., feedstock, loaded in adiabatic reactor.
3. AMC-YJ-02 suitable for purifying natural gas, coking dry gas, catalytic dry gas, hydrogenation dry gas, naphtha etc., feedstock, especially thpse H2 production feedstock with high olefin content, such as catalytic dry gas. It can be filled in adiabatic reactor or column tabular reactor.
Operating conditions
Item | AMC-YJ-01 | AMC-YJ-02 | AMC-YJ-03 |
Temperature/℃ | 180~400 | 160~400 | 180~400 |
Pressure/MPa | 1.0~5.0 | 1.0~5.0 | 1.0~5.0 |
Olefin Content, % | ≤8 | ≤30 | ≤8 |
Organic sulfur content/ppm | ≤300 | ≤300 | ≤300 |
Space velocity/h-1 | ≤3000 | ≤3000 | ≤3000 |
Item | AMC-YJ-01 | AMC-YJ-02 | AMC-YJ-03 |
Color and shape | Grey-green Spherical | Grey-green clover extrudate | Grey-green clover extrudate |
Size/mm | Φ3.5~5.5 | Φ2~3 | Φ2~3 |
Active components | Mo-Co-Ni | Mo-Co-Ni | Mo-Co-Ni |
Carrier | Al2O3-TiO2 | Al2O3-TiO2 | Al2O3-TiO2 |
Bulk density/(kg.L-1) | 0.70~0.90 | 0.50~0.65 | 0.50~0.65 |
Crushing strength | ≥80(N.granula-1) | ≥130(N.cm-1) | ≥130(N.cm-1) |